celanex® 4022 ea4241 white
celanex® 4022 natural
celanex 4022 | pbt | specialty
description
a white pbt resin typically used for applications requiring very opaque parts.
other processing
injection molding
rear temperature 450-470(230-240) deg f (deg c)
center temperature 460-480(235-250) deg f (deg c)
front temperature 470-500(240-260) deg f (deg c)
nozzle temperature 480-500(250-260) deg f (deg c)
melt temperature 460-500(235-260) deg f (deg c)
mold temperature 150-200(65-93) deg f (deg c)
back pressure 0-50 psi
screw speed medium
injection speed fast
injection speed, injection pressure and holding pressure have to be optimized to the inpidual article geometry. to avoid material degradation during processing low back pressure and minimum screw speed have to be used. overheating of the material has to be avoided, in particular for flame retardant grades. up to 25% clean and dry regrind may be used.
iso data physical properties value unit test standard
phys density 1460 kg/m³ iso 1183
mold shrinkage - parallel 1.8-2.0 % iso 294-4
mech mechanical properties value unit test standard
tensile modulus (1mm/min) 3200 mpa iso 527-2/1a
tensile stress at break (5mm/min) 58 mpa iso 527-2/1a
tensile strain at break (5mm/min) 8 % iso 527-2/1a
flexural strength (23℃) 86 mpa iso 178
charpy impact strength @ 23℃ 33 kj/m² iso 179/1eu
charpy notched impact strength @ 23℃ 3.5 kj/m² iso 179/1ea
rockwell hardness 155 m-scale iso 2039-2
therm thermal properties value unit test standard
dtul @ 1.8 mpa 63 ℃ iso 75-1/-2