'cycoloy* resin fxc630me数据
color package may affect performance. pc+abs, eco-conforming flame retardant with metallic or pearlescent appearance.
property
typical properties (1)
mechanical value unit standard
tensile stress,yld,type i,50mm/min 600 kgf/cm² astm d 638
tensile stress,brk,type i,50mm/min 470 kgf/cm² astm d 638
tensile strain,yld,type i,50mm/min 4 % astm d 638
tensile strain,brk,type i,50mm/min 20 % astm d 638
tensile modulus,50mm/min 31600 kgf/cm² astm d 638
flexural stress,yld,1.3mm/min,50mm span 960 kgf/cm² astm d 790
flexural modulus,1.3mm/min,50mm span 27400 kgf/cm² astm d 790
tensile stress,yield,50mm/min 55 mpa iso 527
tensile stress,break,50mm/min 45 mpa iso 527
tensile strain,yield,50mm/min 5 % iso 527
tensile strain,break,50mm/min 15 % iso 527
tensile modulus,1mm/min 2400 mpa iso 527
flexural stress,yield,2mm/min 82 mpa iso 178
flexural modulus,2mm/min 2400 mpa iso 178
hardness,h358/30 99 mpa iso 2039-1
hardness,rockwell r 121 - iso 2039-2
impact value unit standard
izod impact,notched,23℃ 16 cm-kgf/cm astm d 256
instrumented impact total energy,23℃ 483 cm-kgf astm d 3763
izod impact,notched 80*10*4 +23℃ 24 kj/m² iso 180/1a
izod impact,notched 80*10*4 -30℃ 12 kj/m² iso 180/1a
charpy 23℃,v-notch edgew 80*10*4 sp=62mm 25 kj/m² iso 179/1ea
charpy -30℃,v-notch edgew 80*10*4 sp=62mm 13 kj/m² iso 179/1ea
thermal value unit standard
vicat softening temp,rate b/50 98 ℃ astm d 1525
hdt,0.45 mpa,3.2mm,unannealed 90 ℃ astm d 648
hdt,1.82 mpa,3.2mm,unannealed 82 ℃ astm d 648
cte,-40℃ to 40℃,flow 7.20e-05 1/℃ astm e 831
cte,-40℃ to 40℃,xflow 7.20e-05 1/℃ astm e 831
thermal conductivity 0.2 w/m-℃ iso 8302
cte,23℃ to 60℃,flow 8.00e-05 1/℃ iso 11359-2
cte,23℃ to 60℃,xflow 8.00e-05 1/℃ iso 11359-2
ball pressure test,125℃ +/- 2℃ passes - iec 60695-10-2
vicat softening temp,rate b/50 128 ℃ iso 306
vicat softening temp,rate b/120 130 ℃ iso 306
hdt/be,0.45mpa edgew 120*10*4 sp=100mm 128 ℃ iso 75/be
hdt/ae,1.8 mpa edgew 120*10*4 sp=100mm 108 ℃ iso 75/ae
relative temp index,elec 60 ℃ ul 746b
relative temp index,mech w/impact 60 ℃ ul 746b
relative temp index,mech w/o impact 60 ℃ ul 746b
physical value unit standard
specific gravity 1.19 - astm d 792
mold shrinkage,flow,3.2mm(5) 0.3-0.5 % sabic method
melt flow rate,260℃/2.16 kgf 14 g/10 min astm d 1238
density 1.18 g/cm³ iso 1183
density(molded) 1.2 g/cm³ iso 1183
melt volume rate,mvr at 260℃/2.16 kg 14 cm³/10 min iso 1133
melt volume rate,mvr at 260℃/5.0 kg 22 cm³/10 min iso 1133
electrical value unit standard
volume resistivity >1.e+15 ohm-cm iec 60093
surface resistivity,roa >1.e+15 ohm iec 60093
dielectric strength,in oil,0.8mm 35 kv/mm iec 60243-1
dielectric strength,in oil,1.6mm 25 kv/mm iec 60243-1
dielectric strength,in oil,3.2mm 17 kv/mm iec 60243-1
relative permittivity,1 mhz 2.7 - iec 60250
dissipation factor,50/60 hz 0.003 - iec 60250
dissipation factor,1 mhz 0.005 - iec 60250
relative permittivity,50/60 hz 2.8 - iec 60250
flame characteristics value unit standard
ul recognized,94v-2 flame class rating(3) 1.01 mm ul 94
ul recognized,94v-1 flame class rating(3) 1.19 mm ul 94
ul recognized,94v-0 flame class rating(3) 1.49 mm ul 94
ul recognized,94-5vb rating(3) 2 mm ul 94
oxygen index(loi) 23 % iso 4589
source gmd,last updated:2001/04/11
parameter injection molding value unit
drying temperature 80-90 ℃
drying time 3-4 hrs
drying time(cumulative) 8 hrs
maximum moisture content 0.04 %
melt temperature 245-275 ℃
nozzle temperature 245-275 ℃
front-zone 3 temperature 245-275 ℃
middle-zone 2 temperature 220-265 ℃
rear-zone 1 temperature 220-255 ℃
mold temperature 60-80 ℃
back pressure 0.3-0.7 mpa
screw speed 40-70 rpm
shot to cylinder size 30-80 %
vent depth 0.038-0.076 mm
'