OEM Wholesale Ti12mo6zr2fe Titanium Alloy Tube/Pipe for Hip Prosthesis

Product Description

Product Description
Introduction Ti12Mo6Zr2Fe is a BETA titanium alloy without Vanadium developed for orthopaedics. Its properties allow excellent mechanical properties, a low elasticity modulus, a good corrosion and fatigue resistance, besides a good durability. Furthermore, the absence of Aluminium and Vanadium makes it a good biocompatibility.
Composition
The chemical composition of Ti12Mo6Zr2Fe alloy is outlined in the following table.

O	N	C	H	Fe	Mo	Zr	Ti
0,008% min 0,28% max	0% min 0,05% max	0% min 0,05% max	0% min 0,02% max	1,5% min 2,5% max	10,0% min 13,0% max	5,0% min 7,0% max	- Balance

Mechanical Properties of ASTM F1813 Ti12Mo6Zr2Fe Titanium Alloy for Surgical Implant

Property	Value
Tensile Strength (min)	135,000 psi (931.5 MPa)
Yield Strength (0.2% Offset, min)	130,000 psi (897 MPa)
Elongation in 2 in. or 4D (min)	12%
Reduction of Area (min)	30%

Technical Specifications

Specification	Value
Standard	ASTM F1813 Wrought Titanium - 12 Molybdenum - 6 Zirconium - 2 Iron Alloy for Surgical Implant (UNS R58120)
Grade	Ti12Mo6Zr2Fe, β-Ti12Mo6Zr2Fe
Condition & Finish	Descaled or pickled, sandblasted, chemically milled, ground, machined, peeled, polished; Annealed or as rolled
Type	Bar, Wire
Dimension	Bar-Rounds or flats from 3⁄16 in. (4.76 mm) to 4 in.(101.60 mm) in diameter or thickness (other sizes and shapes by special order).
	Wire-Rounds or flats less than 3⁄16 in. (4.76 mm) in diameter or thickness.
Density	4.51g/cm³
Inspection Certificate	EN 10204 Type 3.1 (Mill Test Certificate), EN 10204 Type 3.2 (Witness Testing or 3rd Party Inspection)
Tests	Chemical Composition, Mechanical Properties

Characteristic
High Strength:This alloy offers a high strength-to-weight ratio, which is crucial for implants that need to withstand mechanical stresses without adding excessive weight to the patient's body.
Biocompatibility:Like other titanium alloys, Ti12Mo6Zr2Fe is highly biocompatible, meaning it is not harmful or toxic to living tissue. This reduces the risk of rejection and complications post-surgery.
Corrosion Resistance:The alloy's excellent corrosion resistance ensures the longevity and stability of implants in the harsh environment of the human body.
Improved Wear Resistance:The specific composition of this alloy, including molybdenum, zirconium, and iron, enhances its wear resistance compared to pure titanium. This is particularly important for joint replacements and other implants subject to repetitive motion.
Packing Wire wounded on reel or spool, bars, and rods packed in plywood boxes or on pallets.
Applications Ti12Mo6Zr2Fe (TMZF) alloy is a metastable β-type titanium alloy with the following core medical uses and characteristics in the biomedical field:
I. Main medical uses
Artificial bone implants
TMZF alloy is widely used in bone implants such as artificial hip joints and femoral stems, especially in prosthetic components of biological total hip replacements13.
Orthopedic fixation devices
Used in internal fixation devices such as bone screws, bone plates and implant rods, its mechanical properties can meet the needs of load-bearing bone repair
II. Typical application scenarios
Artificial hip joints: used in conjunction with biological total hip joint systems4.
Dental implants: hard tissue replacement devices such as artificial tooth roots