Corrosion Resistant Gr1 Gr2 Gr3 Gr4 Gr5 Ritanium Plate High Strength Titanium Alloy Plate 6al-4V Titanium Plate ASTM B265 AMS 4911

Product Description

Product Description
Product Parameters

Titanium Plate and sheet Type	Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate
Grade	ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS
Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate Length	1000mm-13000mm or as required
Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Titanium Plate Width	1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required
UNS Plate Thickness	0.3 to 120mm or as required
ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate Process	Hot/ Cold Rolled/forging
UNS Plate surface	No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc.
ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate, Sheet and Strip	JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc
	DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc
Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM	ASTM B265
Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS	AMS 4902
Tolerances of width and thickness	EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V strip (general)
Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals	EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID

Detailed Photos
Daxun produces titanium sheets in China to meet the diverse and --demanding needs of customers!DAXUN produces and stocks commercially pure titanium plates Gr1 Gr2 Gr3 Gr4 (UNS) with thicknesses ranging from 0.5 mm to 120 mm. Gr1 Gr2 Gr3 Gr4 titanium plate (UNS) is the "workhorse" in the commercially pure titanium family. It combines high strength, ductility and excellent corrosion resistance for many industrial applications.
Gr1 Gr2 Gr3 Gr4 titanium plate is a commercially pure titanium plate. It achieves an excellent balance between strength and ductility. It has good impact strength and is easy to weld. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments and wet chlorine. It also has excellent resistance to seawater and salt solutions.
Gr5 grade5 Ti6al4v titanium plate is a titanium alloy plate Gr5 Ti-6Al-4V titanium alloy plate contains 90% titanium, 6% aluminum and 4% vanadium, and is an α-β type titanium alloy, in which aluminum plays the role of stabilizing the α phase and vanadium plays the role of stabilizing the β phase. The main features of Gr5 Ti-6Al-4V titanium alloy plate are excellent comprehensive performance and good process performance. TC4 titanium alloy has excellent room temperature and high temperature strength, good creep resistance and thermal stability, high fatigue performance and crack growth resistance in seawater, as well as satisfactory fracture toughness and hot salt stress corrosion performance. Gr5 Ti-6Al-4V titanium alloy plate also has excellent process plasticity and superplasticity, suitable for various processing methods, as well as various welding and machining methods.
Applications and standardsGr1 Gr2 Gr3 Gr4 Gr5 Titanium Plates have a lower density but higher strength, making them ideal for situations where weight is a concern. Military, medical, chemical equipment, and aerospace are a few key industries for titanium alloys. The strength and corrosion resistance of Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plates also make them ideal for applications in the marine, chemical processing, and desalination industries. Typical applications for Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plates include oil and gas components, reaction and pressure vessels, piping systems, power, heat exchangers, linings, flue gas desulfurization systems, and many other industrial components. Common Standards: ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, AMS4972,
Corrosion Resistance
Gr1 Gr2 Gr3 Gr4 Gr5 titanium plate is highly resistant to seawater and marine atmospheric corrosion. The four C.P. grades have similar corrosion resistance, but their mechanical properties vary depending on the oxygen and iron content. Gr1 Gr2 Gr3 Gr4 Gr5 titanium plate resists attack by wet chlorides and metal chlorides, chlorite and hypochlorite solutions, nitric and chromic acids, organic acids, and many gases for industrial use.
About the chemical composition of(Ti 6AL-4V) grade 5 titanium sheet

Chemical Composition:
Symbol	Element	Min %	Max %
Al	Aluminum	5.50%	6.75%
V	Vanadium	3.50%	4.50%
Fe	Iron		0.30%
O	Oxygen		0.20%
C	Carbon		0.08%
N	Nitrogen		0.05%
H	Hydrogen		0.01%
Y	Yttrium		0.01%
	Other, each		0.10%
	Other, total		0.40%
Ti	Titanium		Remainder

About the mechanical properties of(Ti 6AL-4V) grade 5 titanium sheet

Physical Properties	Metric	English	Comments
Density	4.43 g/cc	0.16 lb/in³
Mechanical Properties
Hardness, Brinell	334	334	Estimated from Rockwell C.
Hardness, Knoop	363	363	Estimated from Rockwell C.
Hardness, Rockwell C	36	36
Hardness, Vickers	349	349	Estimated from Rockwell C.
Tensile strength	min. 895MPa	129810 psi
Yield strength	min. 828MPa	120090 psi
Elongation at Break	min.10 %	10 %
Reduction of Area	min.25 %	25 %

About the chemical composition of grade 2 titanium sheet

Element	Weight %
C	≤0.08
O	≤0.25
N	≤0.03
H	≤0.015
Fe	≤0.30
*OEE	≤0.10
*OET	≤0.40
Ti	Remaining

About the mechanical properties of grade 2 titanium sheet

Alloy	UNS Designation	Spec.	Tensile Strength (min.)			Yield Strength 0.2% Offset (min.)			Elongation in 2 inches (min.)	Max Hardness	Modulus of Elasticity (x106 psi)	Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6)	Thermal Conductivity (BTU-in/ft2-h-°F)
			psi	MPa	ksi	psi	MPa	ksi	%
Grade 2 Titanium	R50400	B338	50,000	-345	50	40,000-	(276-448)	40-65	20	-	16	5.1	144
						50,000

About the chemical composition of grade 1 titanium sheet

Element	Minimum (weight %)	Maximum (weight %)	Typical (weight %)
Fe		0.2
O		0.18
C		0.08
N		0.03
H		0.015
Ti	Balance

About the mechanical properties of grade 1 titanium sheet

Density
lb/in3	g/cm3
0.163	4.51
Tensile Strength
ksi	MPa
35 min	240 min
Yield Strength
ksi	MPa
20 min	138 min
Hardness
70 HRC max
Elongation
24% min

About the chemical composition of 3Al-2.5V titanium sheet
ElementMinimum (weight %)Maximum (weight %)Typical (weight %)

Al	2.5	3.5
V	2.0	3.0
Fe		0.25
O		0.15
C		0.08
N		0.03
H		0.015
Ti	Balance

Packaging & Shipping
Company Profile
Certifications

CP GR1 Titanium plate PHYSICAL PROPERTIES
Physical Properties	Metric	English	Comments
Density	4.50 g/cc	0.163 lb/in³
a Lattice Constant	2.95 Å @Temperature 25.0 °C	2.95 Å @Temperature 77.0 °F	alpha phase
	3.29 Å @Temperature 900 °C	3.29 Å @Temperature 1650 °F	beta phase
c Lattice Constant	4.683 Å	4.683 Å @Temperature 77.0 °F	c/a = 1.587
Mechanical Properties	Metric	English	Comments
Hardness, Brinell	120	120	annealed
Hardness, Knoop	132	132	Estimated from Brinell.
Hardness, Rockwell B	70	70	annealed
Hardness, Vickers	122	122	Estimated from Brinell.
Tensile Strength	124 - 138 MPa @Temperature 427 °C	18000 - 20000 psi @Temperature 801 °F
	152 - 179 MPa @Temperature 316 °C	22000 - 26000 psi @Temperature 601 °F
	193 - 207 MPa @Temperature 204 °C	28000 - 30000 psi @Temperature 399 °F
Tensile Strength, Ultimate	240 MPa	34800 psi
Tensile Strength, Yield	170 - 310 MPa	24700 - 45000 psi
	76.0 - 90.0 MPa @Temperature 427 °C	11000 - 13100 psi @Temperature 801 °F	0.2% offset
	83.0 - 103 MPa @Temperature 316 °C	12000 - 14900 psi @Temperature 601 °F	0.2% offset
	110 - 124 MPa @Temperature 204 °C	16000 - 18000 psi @Temperature 399 °F	0.2% offset
Elongation at Break	24%	24%
	25 - 30 % @Temperature 427 °C	25 - 30 % @Temperature 801 °F
	30 - 35 % @Temperature 316 °C	30 - 35 % @Temperature 601 °F
	40 - 50 % @Temperature 204 °C	40 - 50 % @Temperature 399 °F
Reduction of Area	35%	35%
Tensile Modulus	103 GPa	14900 ksi
Compressive Modulus	110 GPa	16000 ksi
Poissons Ratio	0.37	0.37
Shear Modulus	45.0 GPa	6530 ksi
Charpy Impact	310 J	229 ft-lb	V-notch
Impact Test	136 J	100 ft-lb	Impact Strength
Coefficient of Friction, Dynamic	0.68	0.68	Ti sliding on Ti; 300 m/min
	0.8	0.8	Ti sliding on Ti; 40 m/min

CP GR2 Titanium plate PHYSICAL PROPERTIES
Density	Magnetic Permeability
0.163 lbs/in-3	Nonmagnetic
4.51 g/cm-3	Electrical Resistivity
Beta Transus (+/-25°F, +/--3.9°C)	21 µΩ/in
1680°F	0.53 µΩ/m
915°C	Elastic Modulus
Thermal Conductivity	15.2-17.4 Msi
12.60 BTU hr-1ft-1 °F-1	105-120 GPa
21.79 W m-1 °C-1	Typical values at room temperature of about 68-78°F (20-25°C)

GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES
Physical Properties	Metric	English	Comments
Density	4.43 g/cc	0.16 lb/in³
Mechanical Properties
Hardness, Brinell	334	334	Estimated from Rockwell C.
Hardness, Knoop	363	363	Estimated from Rockwell C.
Hardness, Rockwell C	36	36
Hardness, Vickers	349	349	Estimated from Rockwell C.
Tensile strength	min. 895MPa	129810 psi
Yield strength	min. 828MPa	120090 psi
Elongation at Break	min.10 %	10 %
Reduction of Area	min.25 %	25 %
Modulus of Elasticity	113.8 GPa	16500 ksi
Compressive Yield Strength	970 MPa	141000 psi
Notched Tensile Strength	1450 MPa	210000 psi	Kt (stress concentration factor) = 6.7
Ultimate Bearing Strength	1860 MPa	270000 psi	e/D = 2
Bearing Yield Strength	1480 MPa	215000 psi	e/D = 2
Poisson's Ratio	0.342	0.342
Charpy Impact	17 J	12.5 ft-lb	V-notch
Fatigue Strength	240 MPa	34800 psi	at 1E+7 cycles. Kt (stress concentration factor) = 3.3
Fatigue Strength	510 MPa	74000 psi	Unnotched 10,000,000 Cycles
Fracture Toughness	75 MPa-m½	68.3 ksi-in½
Shear Modulus	44 GPa	6380 ksi
Shear Strength	550 MPa	79800 psi	Ultimate shear strength
Electrical Properties
Electrical Resistivity	0.000178 ohm-cm	0.000178 ohm-cm
Magnetic Permeability	1.00005	1.00005	at 1.6kA/m
Magnetic Susceptibility	3.30E-06	3.30E-06	cgs/g
Thermal Properties
CTE, linear 20°C	8.6 µm/m-°C	4.78 µin/in-°F	20-100ºC
CTE, linear 250°C	9.2 µm/m-°C	5.11 µin/in-°F	Average over the range 20-315ºC
CTE, linear 500°C	9.7 µm/m-°C	5.39 µin/in-°F	Average over the range 20-650ºC
Specific Heat Capacity	0.5263 J/g-°C	0.126 BTU/lb-°F
Thermal Conductivity	6.7 W/m-K	46.5 BTU-in/hr-ft²-°F
Melting Point	1604 - 1660 °C	2920 - 3020 °F
Solidus	1604 °C	2920 °F
Liquidus	1660 °C	3020 °F
Beta Transus	980 °C	1800 °F

A global leader in high performance Ti-6Al-4V titanium plate alloy grade5 titanium plate manufacturing servicesGrade 5
DAXUN is a Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! With the goal of creating the world's high-performance titanium alloy plates. We deliver quickly worldwide - ASTM B265 Grade 2, Grade 5 Titanium Plates. DAXUN produces and stocks alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled. 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is the "workhorse" of titanium alloy materials. It combines high strength, ductility and excellent corrosion resistance, high temperature resistance, thus being favored by many general and military industries. Compliant with: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
Ti-6Al-4V grade 5 titanium plate is mainly used in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, marine industry, etc.
Grade 1
Today, DAXUN Alloys is a leading global producer and supplier of high-quality Grade 1 titanium plate.
Pure Grade 1 titanium plate has excellent ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is known for its excellent general and seawater corrosion resistance, as well as its resistance to oxidizing, neutral and mildly reducing media (solutions), including chlorides. Titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio and corrosion resistance make it an excellent choice for a wide range of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile. It has good cold formability and excellent corrosion resistance. It also has excellent weldability and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the "workhorse" of the commercially pure titanium family. It combines high strength, ductility, and excellent corrosion resistance for many industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate. It offers an excellent balance between strength and ductility. It has good impact strength and is easily weldable. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet chlorine. It also has excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for a wide range of applications, and it effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is a metal expert focused on small and large titanium plate projects. DAXUN is your reference point and long-term partner, ready to provide you and your business with titanium plates and any technical assistance you may need. You can consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates, but also as your strategic partner to help you meet any challenges and needs you may encounter, ultimately allowing you to achieve your project goals.
DAXUN's service center in China has titanium plate products in stock for fast order processing. Through basic processing, water jet cutting and plate nesting products, we provide added value to our customers, saving them time and costs.
Continuous investment in DAXUN's production facilities and capacity agreements with our partners ensure that DAXUN is at the forefront of titanium plate quality now and in the future.
Contact DAXUN today to get the latest titanium plate prices and technical information.
FAQQ1: What products can you offer?
A: We can offer you general steel types like 310S, 316L,304.304L.201,904L, 316H, 316,316L 300and
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce the products according to your drawings that will be most satisfy you.
Q3. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q4. Can I request to change the form of packaging and transportation?
Yes, We can change the form of the packaging and transportation according to your request,
but you have to bear their own costs incurred during this period and the spreads.
Q5. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: 7~20 working days after confirming the payment.
If the order is urgent, we will push our workshop finish in advance.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Order)
B: 30% T/T and balance 70% before the shipment
C: 100% Irrevocable LC at sight (For Big Order)
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Yes, we can. Our material can be used for stainless steel pots, stainless steel sinks, stainless steel bowls etc. U can tell us your usage, and we will adjust the mechanical propertise to meet your requirement.
Q9: How to get a sample?
A: FREE samples are available for your checking and testing.If you require for a small piece,we can afford courier cost,it depends.
Q10:Which country have you exported to?
A:Until now,we have exported stainless steel material to following countries: Vietnam,Thailand,Turkey,Russia,Maroc,Korea,India,Pakistan,UAE,Ukraine and so on.
Q11: How to visit your company?
A:By flight to Guangzhou Baiyun International airport,then we will pick you up.